No-asbestos composite gasket sheet manufactured from no-asbestos beater sheet(asbestos content is about 1-3%)with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.
The construction include:
1) No-asbestos beater sheet + tinplate + no-asbestos beater sheet
2) No-asbestos beater sheet + SS304/316 + no-asbestos beater sheet
Slides Coating Graphite or Silicon Resin
Available Size: Thickness:1.0mm ~ 3.0mm
400mm x 1000mm, 500mm x 1000mm, 500mm x 1200mm,
500mm x 1500mm, 510mm x 1016mm, 1000mm x 1000mm
Color: Gray, Black, Red,Green
The other size is optional or according to the requirements of customers.
Technical Date Sheet
|
Item |
Standard data |
|
|
Density g/cm³ |
1.3～1.5 |
|
|
working temperature ℃ |
-200～250 |
|
|
Compressibility % |
15～20 |
|
|
Recovery ≥ % |
40 |
|
|
causticity |
Cusp no rusty |
|
|
Tensile strength MPa ≥ |
7.0 |
|
|
Compressive Strength MPa ≥ |
80.0 |
|
|
Carbon content ≥ % |
98 |
|
|
Ash content ＜% |
1 |
|
|
With the temperature of 150±2℃,Soaking 20# fluid oil for 5 hours, MPa≥ |
oil absorption %≤ |
25 |
|
Thickness-increasing %≤ |
0～10 |
|
|
Stripping performance |
No stripe |
|
|
With the temperature of 15 to 30℃,Soaking 75# kerosene for 5 hours, MPa≥ |
oil absorption %≤ |
15 |
|
Thickness-increasing %≤ |
0～15 |
|
|
Stripping performance |
No stripe |
|
|
With the temperature of 100℃,Soaking distilled water for 5 hours, MPa≥ |
water absorption %≤ |
15 |
|
Thickness-increasing %≤ |
0～15 |
|
|
Stripping performance |
No strip |
|